White Fused Alumina Granular Sand:
Product Induction:
Our White Fused Alumina is electrically fused in arc furnace under the high temperature of above 2000ºC with high grade processed alumina as raw material. It is divided into a variety of particle sizes after crushing, shaping, magnetic separation and iron removing. The WA is dense texture, the hardness is slightly higher than that of Brown Fused Alumina, with high purity, good self-sharpness, strong grinding force, low calorific value, high efficiency, and acid and alkali corrosion resistance, good temperature stability, etc. White corundum abrasives are widely used in refractory materials, ceramic abrasive tools, resin abrasive tools, coated abrasive tools, grinding and polishing, sand blasting, precision casting and other fields.+
The Chemical Data:
Purpose |
Specification |
(%)Chemical composition(%) | (%) Magnetic material content(%) |
||||
| Al2O3 | Fe2O3 | Na2O | SIO2 | ||||
Sandblasting Abrasives |
F | 12#-80# | ≥99.3 | <=0.15 | <=0.4 | -- | <=0.03 |
| 90#-150# | ≥99.3 | <=0.03 | |||||
| 180#-240# | ≥99.2 | <=0.15 | <=0.4 | -- | <=0.03 | ||
| W | 1#-63# | ≥98.6 | <=0.16 | <=0.4 | <=0.03 | <=0.02 | |
The Physical Data:
Item |
Color |
Color System |
() Mohs Hardness |
(ºC) Melting Temperature(ºC) |
(ºC) Refractory Temperature (ºC) |
(g/cm3) True Density ( g/cm3) |
(%) Magnetic Material (%) |
Specification |
White | Alpha-alumina trigonal system |
≥10 | 2250ºC | 1900ºC | ≥3.50 | 0.01% |
Application: It is suitable for resin abrasives, ceramic abrasives, coated abrasives manufacturing, grinding and polishing, sand blasting and derusting, polishing and grinding, etc.